APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy

Detalhes do produto

Termos do pagamento & do transporte

Quantidade de ordem mínima: 50kg

Preço: Negociável

Detalhes da embalagem: Embalagem de papelão + caixa de madeira

Tempo de entrega: 10-30 dias

Termos de pagamento: T/T

Habilidade da fonte: 500 toneladas/mês

Obtenha o melhor preço

Contacte agora

Especificações

Descrição

Especificações

Destacar: 
                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                                              APM FeCrAl heating strip, high temperature resistance heating strip, Copper Nickel alloy heating wire
                                                  

Material:	Liga fecral	Nota:	APM
Forma:	Tira	Grossura:	0,08-2,80mm
Largura:	10-200 milímetros	Superfície:	Brilhante / Oxidado
Doença:	Macio	Resistividade:	1,53Ω·mm²/m
Temperatura de operação máxima:	1400°C	Processo de Produção:	Metalurgia do Pó
Aplicativo:	Aquecimento de Fornos Industriais	Quantidade mínima:	Negociável

Material:	Liga fecral
Nota:	APM
Forma:	Tira
Grossura:	0,08-2,80mm
Largura:	10-200 milímetros
Superfície:	Brilhante / Oxidado
Doença:	Macio
Resistividade:	1,53Ω·mm²/m
Temperatura de operação máxima:	1400°C
Processo de Produção:	Metalurgia do Pó
Aplicativo:	Aquecimento de Fornos Industriais
Quantidade mínima:	Negociável

Descrição

APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy

Powder Metallurgy APM FeCrAl Heating Alloy Wire up to 1400°C

This product takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electrothermal components, long service life at high temperature and small change of resistance. It is suitable for high temperature 1400 C, high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces,
electronic industrial furnaces and diffusion furnaces.

Main composition

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Main mechanical properties
Tensile Strength at Room Temperature: 650-750MPa
Elongation rate: 15-25%
Hardness: HV220-260
1000ºC Tensile Strength at 1000ºC Temperature 22-27MPa
1000ºC 6MPa High Temperature Durability at 1000 Temperature and 6MPa ≥100h
Main physical properties

Density 7.1g/cm3
Resistivity 1.53×10-6 Ω.m
Resistance Temperature Coefficient(Ct)
Melting point:1500ºC
Maximum Continuous Working Temperature 1400ºC

800ºC	1000ºC	1400ºC
1.03	1.04	1.05

Average linear expansion coefficient

20-800ºC	20-1000ºC	20-1400ºC
14	15	16

Fast life

	1400ºC	1370ºC
Average Fast Life (Hours)	178	>500
Sagging rate after rupture	8	11

1400°C APM Heating Strip for Glass Industry Furnaces Factory price

Tags:

Envie-nos por favor seu pedido e nós responder-lhe-emos o mais cedo possível.

Envie

Fio de liga de cobre níquel

Fio de resistência elétrica

Fio desencapado do par termoeléctrico

Liga de Fecral

Cabo de par termoeléctrico

Liga de Nicr

Fio térmico do pulverizador

Elemento de aquecimento da fornalha

Liga da precisão

Ligação de cobre

Ligação de níquel

Fio esmaltado

Liga de alta temperatura

Conector de par termoelétrico

APM FeCrAl Heating Strip with 1400°C Max Temperature for Industrial Furnace Heating via Powder Metallurgy